Er：YAG 激光不同能量预处理对自粘结树脂水门汀剪切粘结强度的影响

摘要/Abstract

摘要： 目的探讨Er：YAG 激光不同能量预处理对自粘结树脂水门汀剪切粘结强度的影响。方法按照纳入标准收集人离体磨牙70颗，根据对牙本质表面 Er：YAG 激光预处理能量的不同随机分为7组：A组（空白对照）、B组（50 mJ,10 Hz)、C组（100 mJ,10 Hz)、D组（150 mJ,10 Hz)、E组（200 mJ,10 Hz)、F组（250 mJ,10 Hz)、G组（300 mJ,10 Hz)。每组10颗牙中随机取2颗切取3 mm厚的牙本质片，按相应分组用不同激光能量预处理后扫描电镜观察；每组剩余8颗牙包埋后，制备一致标准牙本质表面，按相应分组要求预处理后，用自粘结树脂水门汀RelyXTM Unicem将其与Everest ZS 氧化锆瓷片粘结，24h后测试各组剪切粘结强度并进行统计学分析。结果扫描电镜观察显示Er：YAG 激光预处理后牙本质表面形态改变明显，变得粗糙不平，牙本质小管开放，无玷污层，管周和管间牙本质脱矿，一定能量范围内呈现较好的粘结表面；剪切粘结强度结果显示Er：YAG 激光预处理可增强自粘结树脂水门汀RelyXTM Unicem的剪切粘结强度（P<0.01);C、D、E组的剪切粘结强度与A组有显著性差异（P＜0.05)。结论粘结强度与牙本质的粘结表面密切相关，合适能量下的Er:YAG 激光预处理能获得较好的牙本质粘结表面，提高自粘结树脂与牙本质和氧化锆瓷的剪切粘结强度。

关键词: Er:YAG 激光, 自粘结树脂, 扫描电镜, 剪切粘结强度

Abstract: Objective To investigate the effects of different energies of Er: YAG laser pretreatment on the shear bond strength of self-adhesive resin cement .Methods Seventy extracted human molars collected in accordance with the inclusion criteria were randomly divided into 7 groups according to the different Er:YAG laser energy pretreatments on the dentin surface :Group A (control), GroupB(50 mJ,10 Hz),GroupC(100 mJ,10 Hz),GroupD(150 mJ,10 Hz),GroupE(200 mJ,10 Hz),GroupF(250 mJ,10 Hz),GroupG(300 mJ,10 Hz).Two teeth were selected randomly from each group and 3mm thick dentin slices cut from the teeth were observed under scanning electron microscopy after being pretreated according to the respective requirements .The remaining eight teeth were prepared into the consistent standards dentin surface after being embedded ,and then bonded with the self-adhesive resin cement RelyXTM Unicem and Everest ZS zirconia ceramic after pretreatment according to the respective requirements. 24h later, the shear bond strength was tested and a statistical analysis was performed. Result Scanning electron microscopy showed that the dentin surface morphology pretreated by Er：YAG laser changed into tough irregular one significantly, and the dentinal tubules became open without the smear layer. Peritubular dentin and intertubular dentin suggested demineralization and presented a better bonding surface in a appropriate energy range. The results showed that the Er：YAG laser pretreatment could enhance the bong strength of RelyXTM Unicem self-adhesive resin （P<0.01);there was significant difference between Group C、D、E and Group A（P<0.05).Conclusions The study shows that bond strength is closely related to the dentin bonding surface, and suitable energy of Er：YAG laser pretreatment can obtain better dentin bonding surface, improve the shear bond strength of the self-adhesive resin and dentin and zirconia ceramic.

Key words: Er：YAG laser , self-adhesive resin, SEM, shear bond strength

中图分类号:

R783.1

张晓燕吴凤鸣. Er：YAG 激光不同能量预处理对自粘结树脂水门汀剪切粘结强度的影响[J]. 口腔医学, 2014, 34(12): 931-935.

参考文献

[1] Hibst R,Keller U.Experimental studies of the application of the Er:YAG laser on dental hard substances: I.Measurement of the ablation rate[J]．Lasers Surg Med.1989;9(4):338-44.
[2] Nair PN,Baltensperger MM,Luder HU,et al.Pulpal response to Er:YAG laser drilling of dentin in healthy human third molars[J].Lasers Surg Med.2003,32(3):203-209.
[3] Abdolrahim Davari,Mostafa Sadeghi,Hamid Bakhshi.Shear Bond Strength of an Etch-and-resin Adhesive to Er:YAG Laser-and/or Phosphoric Acid-treated Dentin[J].Dent Res Dent Clin Dent Prospect 2013;7(2):67-73
[4] Giachetti L,Scaminaci Russo D,Scarpelli F,et al .SEM analysis of dentin treated with the Er:YAG laser: a pilot study of the consequences resulting from laser use on adhesion mechanisms.[J].Clin Laser Med Surg.2004,22(1)：35-41.
[5]Andreia Cristina Bastos Ramos,Marcella Esteves-Oliveira,et al. Adhesives bonded to erbium:yttrium–aluminum–garnet laser-irradiated dentin: transmission electron microscopy, scanning electron microscopy and tensile bond strength analyses[J].Lasers Med Sci ，2010，25:181–189.
[6] A.Rüya Yazici,Ishita Agarwal,Marc Campillo-Funollet ,et al.Effect of laser preparation on bond strength of a self-adhesive flowable resin[J].Lasers Med Sci，2013，28;343–347.
[7]Aline Evangelista de Souza,Silmara Aparecida Milori Corona,et al.Influence of Er:YAG laser on tensile bond strength of a self-etching system and a flowable resin in differnt dentin depths[J].Journal of Dentistry,2004,32(4):269-275.
[8] Guven Y,Aktoren O.Shear bond strength and ultrastructural interface analysis of different adhesive system to Er:YAG Laser prepared dentin[J].Lasers Med Sic .2013,28
[9] Eugenia Koliniotou-Koumpia,Pantelis Kouros,Lazaros Zafiriadis,Bonding of adhesive to Er:YAG laser-treated dentin[J].Eur J Dent 2012;6:16-23
[10] 陈利民，王夏衡，王蔚，高平.氧化物陶瓷与3种树脂水门汀初期粘结强度比较[J].实用口腔医学杂志，2010.26（2）：153-156
[11] Rosa D，Aranha A，Eduardo C，et a1．Esthetic treatment of gingival melanin hyperpigmentation with Er：YAG laser：short—term clinical observations and patient follow—up[J]．Journal ofperiodontology，2007，78(10)：2018—2025．
[12] Parnian Alizadeh Oskoee,Narmin Mohammadi,et al.Effect of Surface Treatment with Er;Cr:YSSG,Nd:YAG,and CO2 Laser on Repair Shear Bond Strength of a Silorane-based Composite Resin[J].Dent Res Dent Prospect 2013;7(2):61-66
[13] Hubbezoglu1,Unal M,Zan R,et al.Temperature rises during application of Er:YAG laser under different primary dentin thicknesses[J].Photomed Laser Surg.2013,31(5):201-5
[14] Hossain M,Nakamura Y,Kimura Y,et al.Ablation depths and morphological changes in human enamel and dentin after Er:YAG laser irradiation with or without water mist[J].Clin Laser Med Surg.1999,17(3):105-9
[15] 郭怡丹，张笋.Er：YAG 激光治疗对牙髓的作用[J].中国激光医学杂志,2013，6,22（3）：165-171
[16] Erhan Dilber,Meral Aralan Malkoc,A.Nilgun Ozturk,et al.Effect of various laser irradiations on the mineral content of dentin[J].Eur J Dent 2013;7;74-80.
[17] De Munck J，Vargas M，Van Landuyt K，et a1．Bonding of an auto-adhesive luting material to enamel and dentin[J].Dent Mater,2004．20(10)：963—971．
[18] Rodriguez-Vilchis LE,Contreras-Bulnes R,Olea-Mejia OF,et al.Morphological and structural changes on human dental enamel after Er:YAG laser irradiation:AFM,SEM,and EDS evaluation[J].Photomed Laser Surg,2011,27(7):493-500.