牙本质渗出液对粘接界面的影响

摘要/Abstract

摘要： ［摘要］牙本质渗出液在髓腔压力作用下不断向粘接界面渗出，破坏粘接剂-牙本质粘接界面的完整性，进而降低粘接强度，影响粘接修复的耐久性。该文就牙本质渗出液对不同粘接系统粘接界面、纳米渗漏、粘接强度和在不同牙本质类型中的影响以及改进方法进行综述。

关键词: 牙本质渗出液, 粘接剂, 粘接强度

Abstract: In vital teeth, pulpal pressure causes the continuous outward flow of intrinsic water through the dentinal tubules to the bonding interface,which damages the integrity of the adhesive-dentin bonding interface, and then reduces the bonding strength and affects the durability of adhesive repair.This article contains a brief review of the effects of the outward flow of intrinsic water through the dentinal tubules on the bonding interface, nano-microleakage and bonding strength of different bonding systems.Moreover, this article discusses the measures to reduce the detrimental effects of outward flow of intrinsic water through the dentinal tubules on the bonding interface.

Key words: intrinsic water, dentin bonding systems, bond strength

中图分类号:

R781.05

杨宇斌朱轩言田子璐王惠敏朱松. 牙本质渗出液对粘接界面的影响[J]. 口腔医学, 2020, 40(10): 936-939.

Yu-bin YANG Xuan-Yan ZHU Zi-Lu TIAN Hui-Min WANG. Effect of the intrinsic water on the bonding interface[J]. Stomatology, 2020, 40(10): 936-939.

参考文献 31

[1]	SANO H, CHOWDHURY A F M A, SAIKAEW P, et al.The microtensile bond strength test: Its historical background and application to bond testing[J].The Japanese dental science review, 2020, 56(1):24-31
[2]	SANTANA V B, DE ALEXANDRE R S, RODRIGUES J A, et al.Effects of Immediate Dentin Sealing and Pulpal Pressure on Resin Cement Bond Strength and Nanoleakage[J].Operative Dentistry, 2016, 41(2):189-99
[3]	TJADERHANE L.Dentin Bonding: Can We Make it Last?[J].Operative Dentistry, 2015, 40(1):4-18
[4]	FRASSETTO A, BRESCHI L, TURCO G, et al.Mechanisms of degradation of the hybrid layer in adhesive dentistry and therapeutic agents to improve bond durability-A literature review[J].Dental Materials, 2016, 32(2):E41-E53
[5]	NAGPAL R, MANUJA N, PANDIT I K.Effect of Ethanol Wet Bonding Technique on the Durability of Resin-Dentin Bond with Contemporary Adhesive Systems[J].Journal of Clinical Pediatric Dentistry, 2015, 39(2):133-42
[6]	TAKAMIZAWA T, IMAI A, HIROKANE E, et al.SEM observation of novel characteristic of the dentin bond interfaces of universal adhesives[J].Dental Materials, 2019, 35(12):1791-804
[7]	MALACARNE J, CARVALHO R M, DE GOES M F, et al.Water sorptionsolubility of dental adhesive resins[J].Dental Materials, 2006, 22(10):973-80
[8]	SANAD M, SHEKIDEF M H.The effect of vitality and dentin depth on resin tags length of resin-dentin interface in dogs' teeth[J].Open Veterinary Journal, 2019, 9(2):126-32
[9]	SARTORI N, PERUCHI L D, PHARK J-H, et al.The influence of intrinsic water permeation on different dentin bonded interfaces formation [J]. Journal of Dentistry, 2016, 48(46-54).[J].Journal of Dentistry, 2016, 48:46-54
[10]	HASHIMOTO M, HIROSE N, KITAGAWA H, et al.Improving the durability of resin-dentin bonds with an antibacterial monomer MDPB[J].Dental Materials Journal, 2018, 37(4):620-7
[11]	BRESCHI L, MARAVIC T, CUNHA S R, et al.Dentin bonding systems: From dentin collagen structure to bond preservation and clinical applications[J].Dental Materials, 2018, 34(1):78-96
[12]	KUNAWAROTE S, NAKAJIMA M, FOXTON R M, et al.Effect of pretreatment with mildly acidic hypochlorous acid on adhesion to caries-affected dentin using a self-etch adhesive[J].European Journal of Oral Sciences, 2011, 119(1):86-92
[13]	ITO S, HASHIMOTO M, WADGAONKAR B, et al.Effects of resin hydrophilicity on water sorption and changes in modulus of elasticity[J].Biomaterials, 2005, 26(33):6449-59
[14]	SANO H, TAKATSU T, CIUCCHI B, et al.Nanoleakage: leakage within the hybrid layer[J].Operative dentistry, 1995, 20(1):18-25
[15]	NISHITANI Y, YOSHIYAMA M, WADGAONKAR B, et al.Activation of gelatinolyticcollagenolytic activity in dentin by self-etching adhesives[J].European Journal of Oral Sciences, 2006, 114(2):160-6
[16]	SEZINANDO A, PERDIGAO J, CEBALLOS L.Long-term In Vitro Adhesion of Polyalkenoate-based Adhesives to Dentin[J].Journal of Adhesive Dentistry, 2017, 19(4):305-16
[17]	TAY F R, PASHLEY D H.Water treeing - A potential mechanism for degradation of dentin adhesives[J].American Journal of Dentistry, 2003, 16(1):6-12
[18]	BACCHI A, ABUNA G, BABBAR A, et al.Influence of 3-month Simulated Pulpal Pressure on the Microtensile Bond Strength of Simplified Resin Luting Systems[J].Journal of Adhesive Dentistry, 2015, 17(3):265-71
[19]	TAY F R, PASHLEY D H, SUH B I, et al.Single-step adhesives are permeable membranes[J].Journal of Dentistry, 2002, 30(7-8):371-82
[20]	TAY F R, KING N M, CHAN K-M, et al.How can nanoleakage occur in self-etching adhesive systems that demineralize and infiltrate simultaneously?[J].The journal of adhesive dentistry, 2002, 4(4):255-69
[21]	TAY F R, PASHLEY D H, PETERS M C.Adhesive permeability affects composite coupling to dentin treated with a self-etch adhesive[J].Operative Dentistry, 2003, 28(5):610-21
[22]	BRESCHI L, MAZZONI A, RUGGERI A, et al.Dental adhesion review: Aging and stability of the bonded interface[J].Dental Materials, 2008, 24(1):90-101
[23]	PUCCI C R, GU L-S, ZENG C, et al.Susceptibility of contemporary single-bottle self-etch dentine adhesives to intrinsic water permeation [J]. Journal of Dentistry, 2017, 66(52-61).[J].Journal of Dentistry, 2017, 66:52-61
[24]	FEITOSA V P, SAURO S, ZENOBI W, et al.Degradation of Adhesive-Dentin Interfaces Created Using Different Bonding Strategies after Five-year Simulated Pulpal Pressure[J].Journal of Adhesive Dentistry, 2019, 21(3):199-207
[25]	ZEBIC M L, DZELETOVIC B, MILETIC V.Microtensile bond strength of universal adhesives to flat versus Class I cavity dentin with pulpal pressure simulation[J].Journal of Esthetic and Restorative Dentistry, 2018, 30(3):240-8
[26]	NAKABAYASHI N, SAIMI Y.Bonding to intact dentin[J].Journal of dental research, 1996, 75(9):1706-15
[27]	WANG Y, SPENCER P, YAO X, et al.Effect of coinitiator and water on the photoreactivity and photopolymerization of HEMAcamphoquinone-based reactant mixtures[J].Journal of Biomedical Materials Research Part A, 2006, 78A(4):721-8
[28]	YE Q, PARK J G, TOPP E, et al.In vitro performance of nano-heterogeneous dentin adhesive[J].Journal of Dental Research, 2008, 87(9):829-33
[29]	AGGARWAL V, BHASIN S S.Application of Calcium Silicate Materials After Acid Etching May Preserve Resin-Dentin Bonds [J]. Operative Dentistry, 2018, 43(5).[J].Operative Dentistry, 2018, 43(5):-
[30]	KAVRIK F, KUCUKYILMAZ E.The effect of different ratios of nano-sized hydroxyapatite fillers on the micro-tensile bond strength of an adhesive resin[J].Microscopy Research and Technique, 2019, 82(5):538-43
[31]	SAMIMI P, GHODRATI M, SHIRBAN F, et al.Comparison of the Dentin Bond Strength of Two Self-Etch Adhesives After Prolonged Air-Drying and Additional Light-Curing[J].Journal of dentistry, 2017, 14(5):292-8