Er:YAG激光照射对牙本质粘结强度的影响

Abstract

Abstract: Objective To research the effect of Er:YAG laser irradiation on dentin bonding strength. Methods Forty extracted human premolars or molars were randomly divided into 4 groups : group A，acidetching group (35％ phosphoric acid); group B，Er:YAG laser group; group C，Er:YAG laser + acidetching group; group D，control group. Two teeth selected randomly from each group were cut into 3 mm dentin slices, then observed using scanning electron microscopy(SEM）after treatment. The remaining teeth were prepared into unified dentin bonding surfaces, then combined with resin to test shear bond strength. Results SEM showed that apparent changes occurred to dentin morphology after treatment. The results of statistical analysis showed that group A had the highest shear bond strength (16.03±6.56) MPa and was followed by group C (13.21±6.08) MPa, but there was no significant difference between them（P＞0.05）.Group D had the lowest shear bond strength(4.52±1.02) MPa, and there was no significant difference between group D and group B (7.91±4.56) MPa（P＞0.05）, while there was a significant difference between group D and group A and group C（P<0.05）. Conclusion Compared with Er:YAG laser irradiation alone, acid etching after laser irradiation can enhance the shear bond strength between dentin and resin.

Key words: Er: YAG laser, dentin, SEM, shear bond strength

CLC Number:

R783.1

References

[1]Hubbezoglu I,Unal M,ZanR,et al.Temperature rises during application of Er:YAG laser under different primary dentin thicknesses[J].Photomed Laser Surg,2013,31(5):201-205
[2]Zhang S,Chen T,Ge LH.Scanning electron microscopy study of cavity preparation in deciduous teeth using the Er:YAG laser with different powers[J].Lasers Med Sci,2012,27(1):141-144
[3]Koliniotou-Koumpia E,Kouros P,ZafiriadisL,et al.Bonding of adhesives to Er:YAG laser-treated dentin[J].Eur J Dent,2012,6(1):16-23
[4]Davari A,SadeghiM,Bakhshi H.Shear Bond Strength of an Etch-and-rinse Adhesive to Er:YAG Laser- and/or Phosphoric Acid-treated Dentin[J].J Dent Res Dent Clin Dent Prospects,2013,7(2):67-73
[5]Guven Y,Aktoren O.Shear bond strength and ultrastructural interface analysis of different adhesive systems to Er:YAG laser-prepared dentin[J].Lasers Med Sci,2015,30(2):769-778
[6]张晓燕,吴凤鸣.激光预处理牙本质对树脂粘结性能影响的研究进展[J].口腔医学,2015,35(1):76-80
[7]Kanca J 3rd.Resin bonding to wet substrateII. Bonding to enamel[J]..Quintessence Int,1992,23(9):625-627
[8]Chigira H,Koike T,Hasegawa T,et al.Effect of the self etching dentin primers on the bonding efficacy of a dentin adhesive[J].Dent Mater J,1989,8(1):86-92
[9]Ramos TM,Ramos-Oliveira TM,Esteves-Oliveira M,et al.Effects of Er:YAG and Er,Cr:YSGG laser irradiation on the adhesion to eroded dentin[J].Lasers Med Sci,2015,30(1):17-26
[10]Yazici AR， Agarwal I， Campillo-Funollet M， et al.Effect of laser preparation on bond strength of a self-adhesive flowable resin[J].Lasers Med Sci,2013,28(1):343-347
[11]鄂丽华,达林泰,宝力道,等.Er: YAG 激光处理对牙釉质及牙本质修复效果的影响[J].激光生物学报,2014,23(1):25-
[12]Korkmaz Y,Ozel E,Attar N,et al.Influence of different conditioning methods on the shear bond strength of novel light-curing nanoionomer restorative to enamel and dentin[J].Lasers Med Sci,2010,25(6):861-866
[13]Shirani F,Birang R,Malekipour MR,et al.Shear bond strength of resin composite bonded with two adhesives: Influence of Er: YAG laser irradiation distance[J].Dent Res J,2014,11(6):689-694
[14]李阳,贾兴亚,杜健男.表面处理方法对激光预备牙本质黏结强度的影响[J].中国实用口腔科杂志,2014,7(5):283-286
[15]Rosa D,AranhaA,EduardoC,et al.Esthetic treatment of gingival melanin hyperpigmentation with Er: YAG laser: short-term clinical observations and patient follow-up[J].J Periodontology,2007,78(10):2018-2025
[16]Pashley DH,SanoH,CiucchiB,et al.Adhesion testing of dentin bonding agents : A review[J].Dent Mater,1995,11(2):117-125
[17]PhrukkanonS,BurrowMF,Tyas MJ.The influence of cross-sectional shape and surface area on the microtensile bond test[J].Dent Mater,1998,14(3):212-221

Effect of Er:YAG laser irradiation on dentin bonding strength

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	. Effects of smear layer by different burs on the bonding strength of dentin and self-adhesive resin cement [J]. , 2019, 39(5): 423-426.
[2]	. Study on the effect of the thermal conductivity of crown repair materials on the health of the tooth pulp [J]. , 2019, 39(1): 48-51.
[3]	. Research status of atraumatic restorative treatment and dental caries restoration [J]. , 2018, 38(8): 765-768.
[4]	. Effect of silicon coating via sol-gel self-assembling on the short-term bond strength of zirconia ceramic and resin [J]. , 2018, 38(7): 597-601.
[5]	. Research progress of laser in the treatment of dentin hypersensitivity [J]. , 2018, 38(3): 277-280.
[6]	. Study on the adhesive properties and antibacterial properties of DMAE-CB and NACP modified dentin adhesives [J]. , 2018, 38(3): 227-229.
[7]	Guang Zheng HAN Zheng-Hui XIONG. Influence of ErCr:YSGG Laser Irradiation on adhesion of two adhesive systems to dentin [J]. , 2018, 38(10): 894-897.
[8]	. The effects of tumor necrosis factor-α on the osteogenic/dentinogenic differentiation ability of stem cells from rat apical papilla [J]. , 2017, 37(3): 208-213.
[9]	. Expression of Osterix during Mice dentinogenesis and repairation [J]. , 2017, 37(11): 965-968.
[10]	. Effect of different dentin posts on the stress of resin in filling corner defect of maxillary central incisor [J]. , 2017, 37(11): 986-990.
[11]	. The Progress of Laser Treatment of Dentin Hypersensitivity [J]. , 2017, 37(10): 929-931.
[12]	. Evaluation of the dentin bonding property of a novel universal adhesive under different adhesive modes [J]. , 2016, 36(6): 508-510.
[13]	. In vitro study of the effects of Er:YAG laser irradiation on the shear bond strength of dentin-ceramic interface [J]. , 2016, 36(4): 341-344.
[14]	. Microcosmic and dynamic analysis of the implant-bone interface at early stage in hyperlipidemic rats [J]. , 2016, 36(4): 327-332.
[15]	. The effect of zinc oxide eugenol cement on the shear bond strength of three permanent cements [J]. , 2016, 36(3): 206-209.