牙本质粘接剂新型多用途单体的研究进展

doi:10.13591/j.cnki.kqyx.2025.06.011

摘要/Abstract

摘要：

粘接技术在过去50年里已经取得了巨大的进步,但粘接界面的耐久性依然有一些尚未解决的问题。为了提高牙本质粘接的稳定性,研究者不断尝试开发具有更多种生物功能的粘接剂,例如促进牙本质再矿化、抑制粘接界面酶活性,以及提高胶原蛋白的交联度等功能。本文回顾近几年发表的相关文献,评价具有多种功能的粘接剂单体,希望改进、开发新的粘接剂,降低粘接界面的退化。

关键词: 牙本质, 粘接剂单体, 粘接耐久性

Abstract:

Bonding technology has made tremendous progress over the past 50 years, but there are still some unresolved issues regarding the durability of the bonding interface. In order to improve the durability and stability of dentin bonding, researchers have been trying to develop adhesives with more biological functions, such as promoting dentin remineralisation, inhibiting enzyme activity at the bonding interface, and enhancing collagen cross-linking. Based on the above starting point, this paper evaluates adhesive system monomers with multiple functions through a review of scientific papers published in recent years, in the hope of improving the development of new adhesive systems and reducing the degradation of the bonding interface.

Key words: dentin, adhesive monomers, bonding durability

中图分类号:

R783.1

白庆红, 朱松. 牙本质粘接剂新型多用途单体的研究进展[J]. 口腔医学, 2025, 45(6): 456-459.

BAI Qinghong, ZHU Song. Research progress of novel multifunctional monomers for dentin adhesives[J]. Stomatology, 2025, 45(6): 456-459.

参考文献 37

[1]	Cho K, Rajan G, Farrar P, et al. Dental resin composites: A review on materials to product realizations[J]. Compos Part B Eng, 2022, 230: 109495.
[2]	Breschi L, Maravic T, Cunha SR, et al. Dentin bonding systems: From dentin collagen structure to bond preservation and clinical applications[J]. Dent Mater, 2018, 34(1): 78-96. doi: S0109-5641(17)31120-X pmid: 29179971
[3]	Simmer FS, da Silva EM, Bezerra RDSG, et al. Bond stability of conventional adhesive system with MMP inhibitors to superficial and deep dentin[J]. J Mech Behav Biomed Mater, 2019, 100: 103402.
[4]	Frassetto A, Breschi L, Turco G, et al. Mechanisms of degradation of the hybrid layer in adhesive dentistry and therapeutic agents to improve bond durability: A literature review[J]. Dent Mater, 2016, 32(2): e41-53.
[5]	Sabatini C, Aguilar RJ, Zhang ZW, et al. Mechanical characterization and adhesive properties of a dental adhesive modified with a polymer antibiotic conjugate[J]. J Mech Behav Biomed Mater, 2022, 129: 105153.
[6]	Bourbia M, Ma D, Cvitkovitch DG, et al. Cariogenic bacteria degrade dental resin composites and adhesives[J]. J Dent Res, 2013, 92(11): 989-994. doi: 10.1177/0022034513504436 pmid: 24026951
[7]	Han F, Sun ZD, Xie HF, et al. Improved bond performances of self-etch adhesives to enamel through increased MDP-Ca salt formation phosphoric acid pre-etching[J]. Dent Mater, 2022, 38(1): 133-146.
[8]	Jin X, Han F, Wang Q, et al. The roles of 10-methacryloyloxydecyl dihydrogen phosphate and its calcium salt in preserving the adhesive-dentin hybrid layer[J]. Dent Mater, 2022, 38(7): 1194-1205. doi: 10.1016/j.dental.2022.06.007 pmid: 35715248
[9]	Gimeno A, Beltrán-Debón R, Mulero M, et al. Understanding the variability of the S1' pocket to improve matrix metalloproteinase inhibitor selectivity profiles[J]. Drug Discov Today, 2020, 25(1): 38-57. doi: S1359-6446(19)30341-1 pmid: 31513929
[10]	Swetha R, Gayen C, Kumar D, et al. Biomolecular basis of matrix metallo proteinase-9 activity[J]. Future Med Chem, 2018, 10(9): 1093-1112. doi: 10.4155/fmc-2017-0236 pmid: 29676173
[11]	Singer L, Fouda A, Bourauel C. Biomimetic approaches and materials in restorative and regenerative dentistry: Review article[J]. BMC Oral Health, 2023, 23(1): 105. doi: 10.1186/s12903-023-02808-3 pmid: 36797710
[12]	Oosterlaken BM, Vena MP, de With G. mineralization of collagen[J]. Adv Mater, 2021, 33(16): e2004418.
[13]	Yang QY, Zheng WQ, Zhao YP, et al. Advancing dentin remineralization: Exploring amorphous calcium phosphate and its stabilizers in biomimetic approaches[J]. Dent Mater, 2024, 40(8): 1282-1295. doi: 10.1016/j.dental.2024.06.013 pmid: 38871525
[14]	Zheng H, Shi Y, Bi L, et al. Dual functions of MDP monomer with de- and remineralizing ability[J]. J Dent Res, 2022, 101(10): 1172-1180.
[15]	Teshima I. Degradation of 10-methacryloyloxydecyl dihydrogen phosphate[J]. J Dent Res, 2010, 89(11): 1281-1286. doi: 10.1177/0022034510379018 pmid: 20858773
[16]	Alkattan R, Koller G, Banerji S, et al. Bis[2-(methacryloyloxy)ethyl]phosphate as a primer for enamel and dentine[J]. J Dent Res, 2021, 100(10): 1081-1089.
[17]	Alkattan R, Ajaj R, Koller G, et al. A self-etch bonding system with potential to eliminate selective etching and resist proteolytic degradation[J]. J Dent, 2023, 132: 104501.
[18]	Alakkad T, Burhan R, Alsebyani E, et al. A comprehensive review of the sealing abilities of various root canal sealers[J]. J Healthc Sci, 2023, 3(12): 653-659.
[19]	Morales-Cerrada R, Molina-Gutierrez S, Lacroix-Desmazes P, et al. Eugenol, a promising building block for biobased polymers with cutting-edge properties[J]. Biomacromolecules, 2021, 22(9): 3625-3648.
[20]	Rojo L, Vazquez B, Parra J, et al. From natural products to polymeric derivatives of“eugenol”: A new approach for preparation of dental composites and orthopedic bone cements[J]. Biomacromolecules, 2006, 7(10): 2751-2761.
[21]	Almaroof A, Niazi SA, Rojo L, et al. Evaluation of dental adhesive systems incorporating an antibacterial monomer eugenyl methacrylate(EgMA)for endodontic restorations[J]. Dent Mater, 2017, 33(5): e239-e254.
[22]	Alkattan R, Banerji S, Deb S. A multi-functional dentine bonding system combining a phosphate monomer with eugenyl methacrylate[J]. Dent Mater, 2022, 38(6): 1030-1043.
[23]	Ikeda T, De Munck J, Shirai K, et al. Effect of air-drying and solvent evaporation on the strength of HEMA-rich versus HEMA-free one-step adhesives[J]. Dent Mater, 2008, 24(10): 1316-1323. doi: 10.1016/j.dental.2008.02.009 pmid: 18423839
[24]	Nagakane K, Yoshida Y, Hirata I, et al. Analysis of chemical interaction of 4-MET with hydroxyapatite using XPS[J]. Dent Mater J, 2006, 25(4): 645-649. pmid: 17338295
[25]	Yoshihara K, Yoshida Y, Nagaoka N, et al. Nano-controlled molecular interaction at adhesive interfaces for hard tissue reconstruction[J]. Acta Biomater, 2010, 6(9): 3573-3582.
[26]	Peumans M, Wouters L, De Munck J, et al. Nine-year clinical performance of a HEMA-free one-step self-etch adhesive in noncarious cervical lesions[J]. J Adhes Dent, 2018, 20(3): 195-203. doi: 10.3290/j.jad.a40630 pmid: 29904752
[27]	Fehrenbach J, Isolan CP, Münchow EA. Is the presence of 10-MDP associated to higher bonding performance for self-etching adhesive systems?A meta-analysis of studies[J]. Dent Mater, 2021, 37(10): 1463-1485.
[28]	Ito S, Iijima M, Motai F, et al. Effects of calcium salts of acidic monomers on mineral induction of phosphoprotein immobilized to agarose beads[J]. J Biomed Mater Res A, 2012, 100(10): 2760-2765. doi: 10.1002/jbm.a.34212 pmid: 22623052
[29]	Rao YX, Qiu YJ, Altankhishig B, et al. Novel universal bond containing bioactive monomer promotes odontoblast differentiation in vitro[J]. J Funct Biomater, 2023, 14(10): 506.
[30]	Thaweboon S, Saito T, Nagano K, et al. Evaluation of an adhesive containing calcium salt of acidic monomers on inhibition of biofilm formation of bacteria related to root caries[J]. Key Eng Mater, 2020, 853: 41-45.
[31]	Qiu YJ, Saito T. Novel bioactive adhesive monomer CMET promotes odontogenic differentiation and dentin regeneration[J]. Int J Mol Sci, 2021, 22(23): 12728.
[32]	Qiu YJ, Tang J, Saito T. A novel bio-active adhesive monomer induces odontoblast differentiation: A comparative study[J]. Int Endod J, 2020, 53(10): 1413-1429. doi: 10.1111/iej.13365 pmid: 33460206
[33]	Song LY, Sarikaya R, Ye Q, et al. Multifunctional monomer acts as co-initiator and crosslinker to provide autonomous strengthening with enhanced hydrolytic stability in dental adhesives[J]. Dent Mater, 2020, 36(2): 284-295. doi: S0109-5641(19)30907-8 pmid: 31806495
[34]	Ezazi M, Ye Q, Misra A, et al. Autonomous-strengthening adhesive provides hydrolysis-resistance and enhanced mechanical properties in wet conditions[J]. Molecules, 2022, 27(17): 5505.
[35]	Song LY, Ye Q, Ge XP, et al. Mimicking nature: Self-strengthening properties in a dental adhesive[J]. Acta Biomater, 2016, 35: 138-152. doi: 10.1016/j.actbio.2016.02.019 pmid: 26883773
[36]	Song XZ, Segura-Egea JJ, Díaz-Cuenca A. Sol-gel technologies to obtain advanced bioceramics for dental therapeutics[J]. Molecules, 2023, 28(19): 6967.
[37]	Sarikaya R, Song LY, Ye Q, et al. Evolution of network structure and mechanical properties in autonomous-strengthening dental adhesive[J]. Polymers, 2020, 12(9): 2076.